Garnet-type fast ionic conductor for all-solid-state lithium battery
Rechargeable all-solid-state lithium batteries are expected to be one of the next-generation energy storage devices because of their high energy density, safety, and excellent cycle stability. The materials used for the solid electrolyte must not only have a high lithium-ion conductivity above 1 mS/cm at room temperature, but also possess chemical stability.
Oxide-based solid electrolyte materials have several advantages over sulfide-based ones, such as their chemical stability and ease of handling. Conversely, the formation of a solid-solid interface with low resistance between the solid electrolyte and the electrode is another challenging issue in achieving better electrochemical performance in solid-state batteries with an oxide-based SE.
In this study, Ryoji Inada and his colleagues at the Department of Electrical and Electronic Information Engineering, Toyohashi University of Technology, developed a garnet-type, fast ionic conducting oxide as the solid electrolyte for an all-solid-state battery. Using the developed material, the rechargeable all-solid-state battery was fabricated and tested.
The research team investigated the influence of alien cation (Ba2+ and Ta5+) substitution in Li7La3Zr2O12 (LLZO, Fig. 1) on the crystal phase, microstructure, and ionic conducting property systematically. In order to stabilize the highly conductive cubic garnet phase, the Li concentration in the chemical formulae was fixed at 6.5 so that the formula of the compound may be expressed as Li6.5La3-xBaxZr1.5-xTa0.5+xO12 (LLBZTO).
As a result, the highest room temperature conductivity of 0.83 mS/cm was obtained in LLBZTO garnet with Ba and Ta contents of 0.1 and 1.6, respectively (Fig. 1). The Activation energy of LLBZT garnet tended to decrease monotonically with an increasing Ba substitution level; however, the excess Ba and Ta substitution degraded the conductivity.
In addition, they confirmed that LLBZTO garnet has a wide electrochemical potential window, hence, various positive and negative electrode materials can potentially be utilized to construct an all-solid-state battery. We fabricated a TiNb2O7 (TNO) film electrode on LLBZTO using the aerosol deposition method and demonstrated its charge and discharge reaction using a TNO/LLBZTO /Li all-solid-state battery sample (Fig. 2).
These results indicate that the developed LLBZTO garnet can be used as a solid electrolyte in an all-solid-state battery and contribute to the realization of a very safe rechargeable battery for large-scale power sources, even though additional investigation is needed in order to enhance the performance of solid-state batteries. The researchers carried out further study to realize solid-state batteries with high energy density.
The above research results were reported in Frontiers in Energy Research on July 20, 2016.
This work was partly supported by Grants-in-Aid for Challenging Exploratory Research (Grant No. 26630111) and Scientific Research (C) (Grant No. 16K06218) from the Japan Society for the Promotion of Science (JSPS).
Ryoji Inada, Satoshi Yasuda, Masaru Tojo, Keiji Tsuritani, Tomohiro Tojo and Yoji Sakurai (2016). Development of lithium stuffed garnet-type oxide solid electrolytes with high ionic conductivity for application to all-solid-state batteries, Frontiers in Energy Research 4:28.
Toyohashi University of Technology
1-1 Hibarigaoka, Tempaku
Toyohashi, Aichi Prefecture, 441-8580, JAPAN
Inquiries: Committee for Public Relations
E-mail: [email protected]
Toyohashi University of Technology, which was founded in 1976 as a National University of Japan, is a leading research institute in the fields of mechanical engineering, advanced electronics, information sciences, life sciences, and architecture.